Product Details
Place of Origin: Shandong, China
Brand Name: EXCEED
Certification: ISO 9001:2015
Model Number: A-1170 & B-6003
Payment & Shipping Terms
Minimum Order Quantity: 1 Metric Ton
Price: USD 3000-4000 / Metric Ton
Packaging Details: A-1170: 190kg net per galvanized steel drum; B-6003: 225kg net per galvanized steel drum. 80 drums per 20GP container.
Delivery Time: 7-15 working days after order confirmation
Payment Terms: T/T,L/C
Supply Ability: 5000 Metric Tons per Year
Component A: |
A-1170 (Polyol Blend) |
Component B: |
B-6003 (Isocyanate) |
A-1170 Viscosity (40°C): |
600-1000 MPa·s |
B-6003 Viscosity (40°C): |
500-700 MPa·s |
A-1170 Density (40°C): |
1.01-1.02 G/cm³ |
B-6003 Density (40°C): |
1.08-1.20 G/cm³ |
Mix Ratio (A/B By Weight): |
100 / 103-105 |
Cream Time: |
8-10 Seconds |
End Of Rise Time: |
60-70 Seconds |
Free Rise Foam Density: |
0.30-0.35 G/cm³ |
Molded Density: |
0.50-0.70 G/cm³ |
Hardness: |
70-90 Shore A |
Tear Strength: |
29.5-44.5 KN/m |
Tensile Strength: |
8.0-11.0 MPa |
Elongation: |
335-450% |
Hydrolysis Resistance: |
80°C X 95% Humidity, 14 Days Retained >95% Properties |
Mold Temperature: |
35-45°C |
Demold Time: |
7-9 Minutes |
Shelf Life: |
6 Months |
Component A: |
A-1170 (Polyol Blend) |
Component B: |
B-6003 (Isocyanate) |
A-1170 Viscosity (40°C): |
600-1000 MPa·s |
B-6003 Viscosity (40°C): |
500-700 MPa·s |
A-1170 Density (40°C): |
1.01-1.02 G/cm³ |
B-6003 Density (40°C): |
1.08-1.20 G/cm³ |
Mix Ratio (A/B By Weight): |
100 / 103-105 |
Cream Time: |
8-10 Seconds |
End Of Rise Time: |
60-70 Seconds |
Free Rise Foam Density: |
0.30-0.35 G/cm³ |
Molded Density: |
0.50-0.70 G/cm³ |
Hardness: |
70-90 Shore A |
Tear Strength: |
29.5-44.5 KN/m |
Tensile Strength: |
8.0-11.0 MPa |
Elongation: |
335-450% |
Hydrolysis Resistance: |
80°C X 95% Humidity, 14 Days Retained >95% Properties |
Mold Temperature: |
35-45°C |
Demold Time: |
7-9 Minutes |
Shelf Life: |
6 Months |
A-1170 & B-6003 is a high-performance two-component pu system manufactured by Qingdao Exceed Fine Chemicals Co., Limited. This system combines a polyol blend (A-1170) with an isocyanate component (B-6003) to produce rigid PU foam with excellent hydrolysis resistance and high mechanical strength, specifically engineered for marine fender and shock absorption mat applications.
| Parameter | A-1170 | B-6003 |
|---|---|---|
| Appearance | Liquid | Yellowish transparent liquid |
| Viscosity (40°C) | 600-1000 mPa·s | 500-700 mPa·s |
| Density (40°C) | 1.01-1.02 g/cm³ | 1.08-1.20 g/cm³ |
| Package | 190 kg/drum | 225 kg/drum |
| Parameter | Value |
|---|---|
| Material Preheat | 60-70°C for 8-12 hours (both components) |
| Material Temperature | A: 30-35°C / B: 35-40°C |
| Mix Ratio (A/B by weight) | 100 / 103-105 |
| Cream Time | 8-10 seconds |
| End of Rise Time | 60-70 seconds |
| Mold Temperature | 35-45°C |
| Demold Time | 7-9 minutes |
| Property | Value |
|---|---|
| Hardness | 70-90 Shore A |
| Tear Strength | 29.5-44.5 kN/m |
| Tensile Strength | 8.0-11.0 MPa |
| Elongation | 335-450% |
Test condition: 80°C at 95% humidity. After 14 days of hydrolysis testing, the material retains excellent mechanical integrity with minimal property degradation, making it the ideal choice for long-term marine and high-humidity applications.
A-1170: 6 months | B-6003: 6 months (stored in original sealed containers at recommended conditions).
Contact Qingdao Exceed Fine Chemicals for pricing, samples, and technical consultation.
english
français
Deutsch
Italiano
Русский
Español
português
Nederlandse
ελληνικά
日本語
한국
العربية
हिन्दी
Türkçe
indonesia
tiếng Việt
ไทย
বাংলা
فارسی
polski